20:T4f1,The development of natural hydrogels with sufficient strength and self-healing capacity to accelerate skin wound healing is still challenging. Herein, a hyaluronic acid nanocomposite hydrogel was developed based on aldehyde-modified sodium hyaluronate (AHA), hydrazide-modified sodium hyaluronate (ADA), and aldehyde-modified cellulose nanocrystals (oxi-CNC). This hydrogel was formed in situ using dynamic acylhydrazone bonds via a double-barreled syringe. This hydrogel exhibited improved strength and excellent self-healing ability. Furthermore, platelet-rich plasma (PRP) can be loaded in the hyaluronic acid nanocomposite hydrogels (ADAC) via imine bonds formed between amino groups on PRP (e.g., fibrinogen) and aldehyde groups on AHA or oxi-CNC to promote skin wound healing synergistically. As expected, ADAC hydrogel could protect and release PRP sustainably. In animal experiments, ADAC@PRP hydrogel significantly promoted full-thickness skin wound healing through enhancing the formation of granulation tissue, facilitating collagen deposition, and accelerating re-epithelialization and neovascularization. This self-healing nanocomposite hydrogel with PRP loading appears to be a promising candidate for wound therapy.21:T4b2,Injectable hydrogels as an important biomaterial class have been widely used in regenerative medicine. A series of injectable poly(l-glutamic acid)/alginate (PLGA/ALG) hydrogels were fabricated by self-cross-linking of hydrazide-modified poly(l-glutamic acid) (PLGA-ADH) and aldehyde-modified alginate (ALG-CHO). Both the degree of PLGA modification and the oxidation degree of ALG-CHO could be adjusted by the amount of activators and sodium periodate, respectively. The effect of the solid content of the hydrogels and oxidation degree of ALG-CHO on the gelation time, equilibrium swelling, mechanical properties, microscopic morphology, and in vitro degradation of the hydrogels was examined. Encapsulation of rabbit chondrocytes within hydrogels showed viability of the entrapped cells and good biocompatibility of the injectable hydrogels. A preliminary study exhibited injectability and rapid in vivo gel formation, as well as mechanical stability, cell ingrowth, and ectopic cartilage formation. The injectable PLGA/ALG hydrogels demonstrated attractive properties for future application in a variety of pharmaceutical delivery and tissue engineering, especially in cartilage tissue engineering.

	Year	Citations

References