20:T4db,Subambient daytime radiative cooling (SDRC) provides a promising electricity- and cryogen-free pathway for global energy-efficiency. However, current SDRC systems require stringent surface designs, which are neither cost-effective nor eco-friendly, to selectively emit thermal radiation to outer space and simultaneously maximize solar reflectance. Here, a generic method is developed to upgrade the conventional building-coating materials with a peculiar self-adaptive SDRC effect through combining particle scattering, sunlight-excited fluorescence, and mid-infrared broadband radiation. It is also theoretically proved that heat exchange with the sky can eliminate the use of resonant microstructures and noble metal mirrors in conventional SDRC, and also leads to enhanced daytime cooling yet suppressed nighttime overcooling. When exposed to direct sunlight, the upgraded coating over an aluminum plate can achieve 6 °C (7 °C on a scale-model building) below the ambient temperature under a solar intensity of 744 W m^-2 (850 W m^-2 ), yielding a cooling power of 84.2 W m^-2 . The results pave the way for practical large-scale applications of high-performance SDRC for human thermal comfort in buildings.21:T40c,Passive daytime radiative cooling materials could reduce the energy needed for building cooling up to 60% by reflecting sunlight and emitting long-wave infrared (LWIR) radiation into the cold Universe (~3 kelvin). However, developing passive cooling structures that are both practical to manufacture and apply while also displaying long-term environmental stability is challenging. We developed a randomized photonic composite consisting of a microporous glass framework that features selective LWIR emission along with relatively high solar reflectance and aluminum oxide particles that strongly scatter sunlight and prevent densification of the porous structure during manufacturing. This microporous glass coating enables a temperature drop of ~3.5° and 4°C even under high-humidity conditions (up to 80%) during midday and nighttime, respectively. This radiative "cooling glass" coating maintains high solar reflectance even when exposed to harsh conditions, including water, ultraviolet radiation, soiling, and high temperatures.22:T54e,Daytime radiative coolers are used to pump excess heat from a target object into a cold exterior space without energy consumption. Radiative coolers have become attractive cooling options. In this study, a daytime radiative cooler was designed to have a selective emissive property of electromagnetic waves in the atmospheric transparency window of 8-13 μm and preserve low solar absorption for enhancing radiative cooling performance. The proposed daytime radiative cooler has a simple multilayer structure of inorganic materials, namely, Al₂O₃, Si₃N₄, and SiO₂, and exhibits high emission in the 8-13 μm region. Through a particle swarm optimization method, which is based on an evolutionary algorithm, the stacking sequence and thickness of each layer were optimized to maximize emissions in the 8-13 μm region and minimize the cooling temperature. The average value of emissivity of the fabricated inorganic radiative cooler in the 8-13 μm range was 87%, and its average absorptivity in the solar spectral region (0.3-2.5 μm) was 5.2%. The fabricated inorganic radiative cooler was experimentally applied for daytime radiative cooling. The inorganic radiative cooler can reduce the temperature by up to 8.2 °C compared to the inner ambient temperature during the daytime under direct sunlight.

	Year	Citations

Abstract

References