<i>Trifolium repens</i> L.-Like Periodic Micronano Structured Superhydrophobic Surface with Ultralow Ice Adhesion for Efficient Anti-Icing/Deicing

Abstract

Wind turbine blades are often covered with ice and snow, which inevitably reduces their power generation efficiency and lifetime. Recently, a superhydrophobic surface has attracted widespread attention due to its potential values in anti-icing/deicing. However, the superhydrophobic surface can easily transition from Cassie-Baxter to Wenzel at low temperature, limiting its wide applications. Herein, inspired by the excellent water resistance and cold tolerance of <i>Trifolium repens</i> L. endowed by its micronano structure and low surface energy, a fresh structure was prepared by combining femtosecond laser processing technology and a boiling water treatment method. The prepared icephobic surface aluminum alloy (ISAl) mainly consists of a periodic microcrater array, nonuniform microclusters, and irregular nanosheets. This three-scale structure greatly promotes the stability of the Cassie-Baxter state. The critical Laplace pressure of ISAl is up to 1437 Pa, and the apparent water contact angle (CA) is higher than 150° at 0 °C. Those two factors contribute to its excellent anti-icing and deicing performances. The results show that the static icing delay time reaches 2577 s, and the ice adhesion strength is only 1.60 kPa. Furthermore, the anti-icing and deicing abilities of the proposed ISAl were examined under the environment of low temperature and high relative humidity to demonstrate its effectiveness. The dynamic anti-icing time of ISAl in extreme environments is up to 5 h, and ice can quickly fall with a speed of 34 r/min when it is in a horizontal rotational motion. Finally, ISAl has excellent reusability and mechanical durability, with the ice adhesion strength still being less than 6 kPa and the CA greater than 150° after 15 cycles of icing-deicing tests. The proposed structure would offer a promising strategy for the efficient anti-icing and deicing of wind turbine blades.