Rhenium Suppresses Iridium (IV) Oxide Crystallization and Enables Efficient, Stable Electrochemical Water Oxidation

Abstract

Abstract IrO 2 as benchmark electrocatalyst for acidic oxygen evolution reaction (OER) suffers from its low activity and poor stability. Modulating the coordination environment of IrO 2 by chemical doping is a methodology to suppress Ir dissolution and tailor adsorption behavior of active oxygen intermediates on interfacial Ir sites. Herein, the Re‐doped IrO 2 with low crystallinity is rationally designed as highly active and robust electrocatalysts for acidic OER. Theoretical calculations suggest that the similar ionic sizes of Ir and Re impart large spontaneous substitution energy and successfully incorporate Re into the IrO 2 lattice. Re‐doped IrO 2 exhibits a much larger migration energy from IrO 2 surface (0.96 eV) than other dopants (Ni, Cu, and Zn), indicating strong confinement of Re within the IrO 2 lattice for suppressing Ir dissolution. The optimal catalysts (Re: 10 at%) exhibit a low overpotential of 255 mV at 10 mA cm −2 and a high stability of 170 h for acidic OER. The comprehensive mechanism investigations demonstrate that the unique structural arrangement of the Ir active sites with Re‐dopant imparts high performance of catalysts by minimizing Ir dissolution, facilitating *OH adsorption and *OOH deprotonation, and lowering kinetic barrier during OER. This study provides a methodology for designing highly‐performed catalysts for energy conversion.