Unveiling the Degradation Mechanism of High-Temperature Superconductor Bi₂Sr₂CaCu₂O_8+δ in Water-Bearing Environments

Abstract

(Bi-2212). However, some chemical-related properties of these superconductors are rarely reported, such as their stability in water-bearing environments. Herein, we report experiments combined with ab initio calculations that address the effects of water in contact with Bi-2212. The evolution of Bi-2212 flakes with exposure to water for different time intervals was tested and characterized by optical microscopy (OM), atomic force microscopy (AFM), Raman spectroscopy, transmission electron microscopy (TEM), and electrical measurements. The thickness of Bi-2212 flakes is gradually decreased in water, and some thin flakes can be completely etched away after a few days. The stability of Bi-2212 in other solvents is also evaluated, including alcohol, acetone, HCl, and KOH. The morphology of Bi-2212 flakes is relatively stable in organic solvents. However, the flakes are etched relatively quick in HCl and KOH, especially in an acidic environment. Our results imply that hydrogen ions are primarily responsible for the deterioration of their properties. Both TEM and calculation results demonstrate that the atoms in the Bi-O plane are relatively stable when compared to the inner atoms in Sr-O, Ca-O, and Cu-O planes. This work contributes toward understanding the chemical stability of a Bi-2212 superconducting device in environmental medium, which is important for both fundamental studies and practical applications of copper oxide high-temperature superconductors.