Micro-cracks and micro-fractures reveal radular tooth architecture and its functional significance in the paludomid gastropod <i>Lavigeria grandis</i>

Abstract

Most molluscan taxa forage with their radula, a chitinous membrane with embedded teeth. The teeth are the actual interfaces between the animal and its ingesta and serve as load-transmitting regions. During foraging, these structures have to withstand high stresses without structural failure and without a high degree of wear. Mechanisms contributing to this failure- and wear-resistance were well studied in the heavily mineralized teeth of Polyplacophora and Patellogastropoda, but for the rather chitinous teeth of non-limpet snails, we are confronted with a large gap in data. The work presented here on the paludomid gastropod Lavigeria grandis aims to shed some light on radular tooth composition and its contribution to failure- and wear-prevention in this type of radula. The teeth were fractured and the micro-cracks studied in detail by scanning electron microscopy, revealing layers within the teeth. Two layers of distinct fibre densities and orientations were detected, covered by a thin layer containing high proportions of calcium and silicon, as determined by elemental dispersive X-ray spectroscopy. Our results clearly demonstrate the presence of failure- and wear-prevention mechanisms in snail radulae without the involvement of heavy mineralization—rendering this an example of a highly functional biological lightweight structure. This article is part of the theme issue 'Nanocracks in nature and industry'.