Early bone formation around calcium‐ion‐implanted titanium inserted into rat tibia

Abstract

Rat tibia tissue into which calcium ion (Ca2+)-implanted titanium was surgically placed was histologically analyzed to investigate the performance of the Ca2+-implanted titanium as a biomaterial. Calcium ions were implanted into only one side of titanium plates at 1017 ions/cm2 and the Ca2+-treated titanium was surgically implanted into rat tibia for 2, 8, and 18 days. Tetracycline and calcein were used as hard-tissue labels. After excision of the tibia, the tissues were fixed, stained, embedded in polymethyl methacrylate, and sliced. The specimens were observed using a fluorescence microscope. A larger amount of new bone was formed on the Ca2+-treated side than on the untreated side, even at 2 days after surgery. In addition, part of the bone made contact with the Ca2+-treated surface. On the other hand, bone formation on the untreated side was delayed and the bone did not make contact with the surface. Mature bone with bone marrow formed in 8 days. Neither macrophage nor inflammatory cell infiltration was observed. The results indicated that Ca2+-implanted titanium is superior to titanium alone for bone conduction. © 1997 John Wiley & Sons, Inc. J Biomed Mater Res, 36, 131–136, 1997.