Controlled optimization of Mg and Zn in Al alloys for improved corrosion resistance <i>via</i> uniform corrosion

Abstract

The inclusion of trace amounts of Mg and Zn to Al alloys caused the development of β and τ phases at the grain boundary, resulting in the change from pitting corrosion to intergranular corrosion and therefore increased corrosion resistance.