Enhanced Electromagnetic-Wave Absorbing Performances and Corrosion Resistance via Tuning Ti Contents in FeCoNiCuTi_<i>x</i> High-Entropy Alloys

Abstract

Efficient and stable electromagnetic-wave (EMW) absorption materials have attracted great attention in the field of reducing microwave pollution. Herein, FeCoNiCuTi_<i>x</i> high-entropy alloys (HEAs) as electromagnetic-wave absorbing materials were prepared by a high-energy ball-milling method. The as-milled HEA powders presented a flaky shape with a high aspect ratio. Impedance matching was efficiently optimized by severe lattice distortion, which was caused by Ti incorporation. The introduced plentiful defects in FeCoNiCuTi_<i>x</i> HEAs provided abundant polarization sites for dielectric loss. By tuning Ti contents, FeCoNiCuTi_0.2 HEAs delivered excellent EMW absorption performances. The maximal reflection loss (RL_max) values reached -47.8 dB at 10.86 GHz as thin as 2.16 mm, and the widest bandwidth was 4.76 GHz (5.97-10.73 GHz). Furthermore, the introduction of Ti enhanced corrosion resistance via increasing the charge transfer resistance of a passivated film. Those characteristics of FeCoNiCuTi_<i>x</i> HEAs made these materials a practical gigahertz-range EMW absorber. Additionally, our findings provided a facile and tunable strategy for designing EMW absorbing materials, which was aimed at lightweight, highly efficient absorption, and resistance to harsh environments.