Ultra‐High Fluorine Enhanced Homogeneous Nucleation of Lithium Metal on Stepped Carbon Nanosheets with Abundant Edge Sites

Abstract

Abstract Disordered nucleation sites and a fragile solid electrolyte interphase on the reactive interface tend to cause uncontrolled growth of lithium dendrites, which induce severe safety concerns and prevent lithium metal batteries from finding practical applications. Herein, novel stepped carbon nanosheets with abundant step edges and ultra‐high fluorine content (37.44 at%) are fabricated by combining an improved molten salt synthesis method with C 4 F 8 vacuum plasma treatment. The solvent‐induced spatial confinement effect, i.e., orientation carbonization of pitch macromolecules, leads to the formation of step‐edge‐enriched nanoarrays. Meanwhile, the adequate exposure of edge sites on the basal plane of carbon nanosheets is conducive to achieve the ultra‐efficient doping of elemental fluorine in only 10 min. Further experiments and theoretical calculations demonstrate that the coupling effect of sufficient edge sites and active semi‐ionic CF/covalent CF 2 groups on the carbon surface can not only form 2D fluorinated lithium chain and a robust LiF network, but also effectively facilitate Li ion redox kinetics and morphological stability, presenting a step‐edge‐guided plating process. As such, the developed anodes deliver an ultra‐low nucleation overpotential (≈10.5 mV), high Coulombic efficiency (>98% over 385 cycles), ultra‐long cycling duration for up to 3000 h under ≈10 mV, and excellent full battery performance.