Bi(Mg<sub>1/2</sub>Zr<sub>1/2</sub>)O<sub>3</sub>–PbZrO<sub>3</sub>–PbTiO<sub>3</sub> relaxor ferroelectric ceramics with large and temperature-insensitive electric field-induced strain response
11
Citations
36
References
2021
Year
Materials EngineeringMaterials ScienceMultiferroicsHigh Temperature StabilityEngineeringFerroelectric ApplicationCeramic MaterialApplied PhysicsCondensed Matter PhysicsFerroelectric MaterialsCeramics MaterialsLarge StrainPzt CeramicsFunctional MaterialsEngineering CeramicStructural CeramicMagnetoelectric Materials
A large strain (0.33% at 5 kV mm −1 ) and high temperature stability (strain variation less than 8%) were obtained simultaneously in new BMZ-PZ-PT ternary ceramics by the substitution of BMZ for PZ in PZT ceramics.