Combined Precursor Engineering and Grain Anchoring Leading to MA‐Free, Phase‐Pure, and Stable α‐Formamidinium Lead Iodide Perovskites for Efficient Solar Cells

Abstract

Abstract α‐Formamidinium lead iodide (α‐FAPbI 3 ) is one of the most promising candidate materials for high‐efficiency and thermally stable perovskite solar cells (PSCs) owing to its outstanding optoelectrical properties and high thermal stability. However, achieving a stable form of α‐FAPbI 3 where both the composition and the phase are pure is very challenging. Herein, we report on a combined strategy of precursor engineering and grain anchoring to successfully prepare methylammonium (MA)‐free and phase‐pure stable α‐FAPbI 3 films. The incorporation of volatile FA‐based additives in the precursor solutions completely suppresses the formation of non‐perovskite δ‐FAPbI 3 during film crystallization. Grains of the desired α‐phase are anchored together and stabilized when 4‐ tert ‐butylbenzylammonium iodide is permeated into the α‐FAPbI 3 film interior via grain boundaries. This cooperative scheme leads to a significantly increased efficiency close to 21 % for FAPbI 3 perovskite solar cells. Moreover, the stabilized PSCs exhibit improved thermal stability and maintained ≈90 % of their initial efficiency after storage at 50 °C for over 1600 hours.