Optimization on thermoelectric characteristics of indium tin oxide/indium oxide thin film thermocouples based on screen printing technology

Abstract

In this work, indium tin oxide (ITO)/indium oxide (In₂O₃) thin film thermocouples (TFTCs) were prepared based on screen printing technology for high temperature measurement. With terpilenol as solvent, epoxy resin and polyether amine as binders and glass powders as additives, the ITO and In₂O₃ slurries were printed onto the Al₂O₃ substrate to form thermocouples. The effect on thermoelectric properties of the TFTCs with heat treatment and different contents of additives was investigated through microstructure observation and thermal cycle test. The static calibration experiment shows that the annealed TFTCs with 7.5 wt. % glass powders additives have the maximum Seebeck coefficient. The thermoelectric voltage output of the TFTCs can reach 126.5 mV at 1275 °C while the temperature difference is 1160 °C and the sensitivity of the TFTCs was 109.1 µV/°C. The drift rate of the TFTCs was 8.34 °C/h at a measuring time of 20 min at 1275 °C. The TFTCs prepared via screen printing technology with excellent thermoelectric properties and thermal stability are aimed to be a viable replacement for practical applications.