An Improved Nonlinear Cumulative Damage Model Considering the Influence of Load Sequence and Its Experimental Verification

Abstract

According to the change characteristics in the toughness of the metal material during the fatigue damage process, the fatigue tests were carried out with the standard 18CrNiMo7-6 material. Scanning the fracture with an electron microscope explains the lack of linear cumulative damage in the mechanism. According to the obtained results, a nonlinear damage accumulation model which considered the loading sequence state under the toughness dissipation model was established. The recursive formula was devised under two-level. The fatigue test data verification of three metal materials showed that using this model to predict fatigue life is satisfactory and suitable for engineering applications.