Comparative Study of Red/Green/Blue Quantum-Dot Light-Emitting Diodes by Time-Resolved Transient Electroluminescence

Abstract

To understand the electronic processes in quantum-dot light-emitting diodes (QLEDs), a comparative study was performed by time-resolved transient electroluminescence (TREL). We fabricated red, green, and blue (R-, G-, and B-) QLEDs with poly(9,9-dioctylfluorene-<i>co</i>-<i>N</i>-(4-<i>sec</i>-butylphenyl)diphenylamine) as the hole-transporting layer with conventional structures. The external quantum efficiency (EQE) and current efficiency were 19.2% and 22.7 cd A^-1 for R-QLEDs, 21.1% and 93.3 cd A^-1 for G-QLEDs, and 10.6% and 10.4 cd A^-1 for B-QLEDs, respectively. The TREL results for B-QLEDs were remarkably different from those for R- and G-QLEDs because of the insufficient electron injection crossing the type II heterojunction between the emission layer and the electron-transporting layer. We further applied poly(<i>N</i>-vinylcarbazole) as the hole-transporting layer and obtained much better performance for B-QLEDs, with EQE and current efficiency of 15.9% and 15.4 cd A^-1, respectively. Concomitant with the increase in EQE are an increase in the turn-on voltage from 2.3 to 3.7 V and a transient electroluminescence spike after voltage turn-off.