Control of Phase Morphology of Binary Polymer Grafted Nanoparticle Blend Films <i>via</i> Direct Immersion Annealing

Abstract

While the phase separation of binary mixtures of chemically different polymer-grafted nanoparticles (PGNPs) is observed to superficially resemble conventional polymer blends, the presence of a "soft" polymer-grafted layer on the inorganic core of these nanoparticles <i>qualitatively</i> alters the phase separation kinetics of these "nanoblends" from the typical pattern of behavior seen in polymer blends and other simple fluids. We investigate this system using a direct immersion annealing method (DIA) that allows for a facile tuning of the PGNPs phase boundary, phase separation kinetics, and the ultimate scale of phase separation after a sufficient "aging" time. In particular, by switching the DIA solvent composition from a selective one (which increases the interaction parameter according to Timmerman's rule) to an overall good solvent for both PGNP components, we can achieve rapid switchability between phase-separated and homogeneous states. Despite a relatively low and non-classical power-law coarsening exponent, the overall phase separation process is completed on a time scale on the order of a few minutes. Moreover, the roughness of the PGNP blend film saturates at a scale that is proportional to the in-plane phase separation pattern scale, as observed in previous blend and block copolymer film studies. The relatively low magnitude of the coarsening exponent <i>n</i> is attributed to a suppression of hydrodynamic interactions between the PGNPs. The DIA method provides a significant opportunity to control the phase separation morphology of PGNP blends by solution processing, and this method is expected to be quite useful in creating advanced materials.