Link between Structural and Optical Properties of Co_<i>x</i>Fe_3–<i>x</i>O₄ Nanoparticles and Thin Films with Different Co/Fe Ratios

Abstract

CoxFe3–xO4 nanoparticles (x = 0.4 to x = 2.5) and thin films (x = 0.9 to x = 2.2) are analyzed by Raman, absorption, and photoluminescence spectroscopy to link structural and optical properties to different cobalt to iron (Co/Fe) ratios. Raman spectroscopy shows that with decreasing Co content, the crystal structure changes from a predominantly normal cubic spinel phase to a mixed inverse spinel phase. This finding is supported by absorption spectroscopy that points out that inter valence charge transfer (IVCT) processes between octahedrally coordinated Co2+ and Fe3+ cations become more prominent with increasing Fe content. Independent of the Co/Fe ratio, CoxFe3–xO4 nanoparticles show a broad photoluminescence (PL) band with a maximum at around 510 nm. Time-resolved photoluminescence spectroscopy shows subnanosecond lifetimes and temperature-resolved photoluminescence experiments reveal that the green PL increases with decreasing temperature (300 to 10 K) while showing no temperature-dependent shift in energy. It is proposed that this green PL originates from OH-groups on the particles’ surface.