The properties and high-efficiency potential of front- and rear-emitter silicon heterojunction solar cells on n- and p-type wafers were experimentally investigated. In the low-carrier-injection range, cells on p-type wafers suffer from reduced minority carrier lifetime, mainly due to the asymmetry in interface defect capture cross sections. This leads to slightly lower fill factors than for n-type cells. By using high-quality passivation layers, however, these losses can be minimized. High open-circuit voltages ( V _oc s) were obtained on both types of float zone (FZ) wafers: up to 735 mV on n-type and 726 mV on p-type. The best V _oc measured on Czochralski (CZ) p-type wafers was only 692 mV, whereas it reached 732 mV on CZ n-type. The highest aperture-area certified efficiencies obtained on 4 cm ² cells were 22.14% ( V _oc = 727 mV , FF = 78.4%) and 21.38% ( V _oc = 722 mV, FF = 77.1%) on n- and p-type FZ wafers, respectively, proving that heterojunction schemes can perform almost as well on high-quality p-type as on n-type wafers. To our knowledge, this is the highest efficiency ever reported for a full silicon heterojunction solar cell on a p-type wafer, and the highest V _oc on any p-type crystalline silicon device with reasonable FF.

	Year	Citations

References