On the Colloidal Stability of PbS Quantum Dots Capped with Methylammonium Lead Iodide Ligands

Abstract

Phase-transfer exchange of pristine organic ligands for inorganic ones is essential for the integration of colloidal quantum dots (CQDs) in optoelectronic devices. This method results in a colloidal dispersion (ink) which can be directly deposited by various solution-processable techniques to fabricate conductive films. For PbS CQDs capped with methylammonium lead iodide ligands (MAPbI₃), the most commonly employed solvent is butylamine, which enables only a short-term (hours) colloidal stability and thus brings concerns on the possibility of manufacturing CQD devices on a large scale in a reproducible manner. In this work, we studied the stability of alternative inks in two highly polar solvents which impart long-term colloidal stability of CQDs: propylene carbonate (PC) and 2,6-difluoropyridine (DFP). The aging and the loss of the ink's stability were monitored with optical, structural, and transport measurements. With these solvents, PbS CQDs capped with MAPbI₃ ligands retain colloidal stability for more than 20 months, both in dilute and concentrated dispersions. After 17 months of ink storage, transistors with a maximum linear mobility for electrons of 8.5 × 10^-3 cm²/V s are fabricated; this value is 17% of the one obtained with fresh solutions. Our results show that both PC- and DFP-based PbS CQD inks offer the needed shelf life to allow for the development of a CQD device technology.