P-Type-to-N-Type Transition in Hybrid Ag_xTe/PEDOT:PSS Thermoelectric Materials via Stoichiometric Control during Solution-Based Synthesis

Abstract

This work demonstrates the production of high-performing p- type and n-type hybrid AgxTe/poly(3,4-ethylenedioxythiopene):polystyrene sulfonic acid (PE-DOT:PSS) thermoelectric materials from the same Te/PEDOT:PSS parent structure during aqueous-based synthesis. All samples were solution-processed and analyzed in thin- film architectures. We were able to demonstrate a power factor of 44 mu W m(-1) K-2 for our highest-performing n-type material. In addition, we were also able to realize a 68% improvement in the power factor of our p-type compositions relative to the parent structure through manipulation of the inorganic nanostructure composition. We demonstrate control over the thermoelectric properties by varying the stoichiometry of AgxTe nanoparticles in AgxTe/PEDOT:PSS hybrid materials via a topotactic chemical transformation process at room temperature. This process offers a simple, low-temperature, and cost-effective route toward the production of both efficient n-type and p-type hybrid thermoelectric materials.