Magnetic tunnel junctions with metastable bcc Co₃Mn electrodes

Abstract

We studied magnetic tunnel junctions (MTJs) with a MgO(001) barrier and metastable bcc Co3Mn(001) disordered alloy electrodes. A tunnel magnetoresistance (TMR) ratio was approximately 200{250% observed at room temperature.We successfully observed the TMR ratio greater than 600% at 10 K which was higher than the past reported value of MgO-based MTJs with ultrathin bcc Co(001) electrodes. However our experimental value was still much lower than the past theoretical prediction in bcc Co/MgO/Co(001) MTJs. We discuss some differences in the bulk band structure affecting the TMR effect for bcc Co and bcc Co3Mn.