Zirconium-based metallic glass and zirconia coatings to inhibit bone formation on titanium

Abstract

Surface-modified commercially pure titanium (Cp-Ti) with zirconium (Zr)-based thin film metallic glasses (Zr-TFMGs) and ZrO₂ thin films were surgically implanted into the tibiae of rats; the bone formation was analyzed to examine the performance of the coatings as a biomaterial. Zr-TFMGs and ZrO₂ thin films were coated on Cp-Ti substrates to monitor the control of assimilation in vitro and in vivo. The microstructural and elemental analyses were carried out for the as deposited thin films by x-ray diffraction (XRD), transmission electron microscopy and x-ray photoelectron spectroscopy. TFMG- and ZrO₂-coated Ti specimens were immersed in simulated body fluid (SBF) for a period of 21 days to evaluate the calcium phosphate precipitation in vitro. XRD, x-ray photoelectron spectroscopy and scanning electron microscopy/energy dispersive x-ray spectroscopy were used to quantify the mineralization on the coated Zr-TFMG and ZrO₂. In vitro corrosion studies showed that the Zr-based TFMG and ZrO₂ coatings sustained in the SBF, exhibited superior corrosion resistance to the bare crystalline Ti substrate. Wettability studies showed TFMG and ZrO₂ coatings with a hydrophobic nature, and the TFMG-coated SBF-submerged specimens showed a hydrophilic nature. The in vitro cell viability of MC3T3-E1 cells showed good cell proliferation and low cytotoxicity. The calcification deposits were evaluated by staining with alizarin red S, which showed a lower calcium formation on Zr-TFMG compared to ZrO₂. The present work also aims to assess the assimilation behavior of Cp-Ti, Zr-TFMG and ZrO₂ in vivo by inserting the coated specimen in the femur of rats. After post-implantation of 8 weeks, specimens were examined by micro-CT evaluation. The bone contact ratios as calculated were 72.75%, 15.32% and 38.79%. Consequently, the bone affinity was Cp-Ti wire >ZrO₂-coated Ti wire >Zr₄₈Cu₃₆Ag₈Al₈-coated Ti wire.