Toughness Deterioration and Its Improvement of Weld HAZ with High Heat Inputs in 780 and 980MPa Class HSLA Steels(Report 2). Metallographic Investigation of M-A Constituent.

Abstract

The internal microstructure, chemical composition, and hardness of M-A (Martensite-Austenite constituent) formed in weld CGHAZ (Coarse Grained Heat Affected Zone) of 780-980 MPa class HSLA steels have been investigated in order to reveal metallographic characteristics of the M-A constituent. The martensite was classified into lath and twin type. The massive M-A constituent had higher C contents, and included more twin type martensite and retained austenite than the elongated M-A. The cementite was found to be classified into a coarse rod type and a dendritic or fine needle type. The coarse rod type is considered to be precipitated directly from the austenite. The dendritic or fine needle type is probably precipitated by the self tempering of martensite.