Titania–Samarium–Manganese Composite Oxide for the Low-Temperature Selective Catalytic Reduction of NO with NH₃

Abstract

A novel Ti-doped Sm–Mn mixed oxide (TiSmMnOx) was first designed for the selective catalytic reduction (SCR) of NOx with NH3 at a low temperature. The TiSmMnOx catalyst exhibited a superior catalytic performance, in which NOx conversion higher than 80% and N2 selectivity above 90% could be achieved in a wide-operating temperature window (60–225 °C). Specially, the catalyst also showed high durability against the large space velocity and excellent SO2/H2O resistance. Ti incorporation can efficiently inhibit MnOx crystallization and tune the MnOx phase during calcination at a high temperature. Subsequently, a high specific surface area as well as an increased amount of acid sites on the TiSmMnOx catalysts were produced. Further, the reducibility of the Sm-doped MnOx catalyst was modulated, facilitating NO oxidation and inhibiting NH3 nonselective oxidation. Consequently, a superior SCR activity was achieved at a low temperature and the operating temperature window of the TiSmMnOx catalyst was significantly widened. These findings may provide new insights into the reasonable design and development of the new non-vanadium catalysts with a high NH3-SCR activity for industrial application.