Structure evolution of bio-based PLA/ENR thermoplastic vulcanizates during dynamic vulcanization processing

Abstract

The thermoplastic vulcanizates (TPVs) of Polylactide (PLA)/Epoxidized natural rubber (ENR) were prepared by dynamic vulcanization technology. The processing torque, crosslink density, morphology of PLA/ENR blends, and PLA's molecular weight during the processing were investigated by HAAKE rheometer, swelling measurement, scanning electron microscopy (SEM), and gel permeation chromatography (GPC). It was found that the vulcanization of ENR completed at the turning point after torque peak. After the turning point, the torque and crosslink density decreased with the processing time increasing. Moreover, the morphology of PLA/ENR blends showed bi-continuous structure during the dynamic vulcanization processing, and the phase size of PLA/ENR was increased with processing time and temperature. GPC results showed PLA degradation mainly happened after torque turning point. Thermal gravimetric analysis (TGA) results indicated that some parts of PLA would graft on ENR during processing, and the higher the processing temperature, the more the PLA was grafted.