Enhancement of resistance to galvanic corrosion of ZE41 Mg alloy by equal channel angular pressing

Abstract

Abstract The galvanic corrosion behavior of as‐received and ECAPed ZE41 Mg alloy coupled with Al7075 alloy is investigated using zero resistance ammeter in three different corrosive environments, 0, 0.1, and 1 M NaCl, to mimic the conditions experienced in engineering applications. The mechanism of galvanic corrosion for the ZE41 Mg–Al7075 aluminum alloy is explained. It is observed that a robust surface film containing a composite layer of oxide/hydroxide of magnesium and aluminum is established in deionized water (0 M). However, only a single layer of magnesium oxide/hydroxide is detected in chloride‐containing environments. Equal channel angular pressing (ECAP) improved the resistance to galvanic corrosion by 58% and 54% when compared with the as‐cast counterparts in 0 and 1 M NaCl solution, respectively. In contrast, galvanic corrosion resistance decreased by 26% in 0.1 M NaCl after ECAP while the as‐received samples evinced pits unfavorable to be used in engineering applications. ECAP is a promising method to combat galvanic corrosion encountered by ZE41 magnesium alloy used in automobiles and components of military vehicles.