Afterglow, TL and OSL properties of Mn2+-doped ZnGa2O4 phosphor

Abstract

Abstract Zinc gallate (ZnGa 2 O 4 ) spinel ceramics doped with Mn 2+ ions was prepared by a solid-state reaction at 1200 °C in air. Manganese concentration was equal to 0.05 mol.% of MnO with respect to ZnO. Ceramics produced in this way show an efficient green emission at about 505 nm under UV or X-ray excitations, which is caused by Mn 2+ ions. This green emission is observed also as a relatively long afterglow (visible to the naked eye in the dark for about one hour) after switching-off the X-ray excitation. Time profiles of the beginning of glow and afterglow have been studied together with thermally stimulated (TSL) and optically stimulated (OSL) luminescence. Experimental results demonstrate a presence of few types of shallow and deep traps responsible for the observed afterglow and TSL/OSL emission of the material. The possibility of pulsed optical stimulation and time-resolved OSL characteristics of ZnGa 2 O 4 : Mn 2+ has been reported for the first time. The presented results suggest the ZnGa 2 O 4 : Mn 2+ spinel as a promising material for further fundamental research and possibility of application as a green long-lasting phosphor or storage phosphor for TSL/OSL radiation dosimetry.