A Simple Synthetic Strategy toward Defect‐Rich Porous Monolayer NiFe‐Layered Double Hydroxide Nanosheets for Efficient Electrocatalytic Water Oxidation

Abstract

Abstract In this work, porous monolayer nickel‐iron layered double hydroxide (PM‐LDH) nanosheets with a lateral size of ≈30 nm and a thickness of ≈0.8 nm are successfully synthesized by a facile one‐step strategy. Briefly, an aqueous solution containing Ni 2+ and Fe 3+ is added dropwise to an aqueous formamide solution at 80 °C and pH 10, with the PM‐LDH product formed within only 10 min. This fast synthetic strategy introduces an abundance of pores in the monolayer NiFe‐LDH nanosheets, resulting in PM‐LDH containing high concentration of oxygen and cation vacancies, as is confirmed by extended X‐ray absorption fine structure and electron spin resonance measurements. The oxygen and cation vacancies in PM‐LDH act synergistically to increase the electropositivity of the LDH nanosheets, while also enhancing H 2 O adsorption and bonding strength of the OH* intermediate formed during water electrooxidation, endowing PM‐LDH with outstanding performance for the oxygen evolution reaction (OER). PM‐LDH offers a very low overpotential (230 mV) for OER at a current density of 10 mA cm −2 , with a Tafel slope of only 47 mV dec −1 , representing one of the best OER performance yet reported for a NiFe‐LDH system. The results encourage the wider utilization of porous monolayer LDH nanosheets in electrocatalysis, catalysis, and solar cells.