Realizing super-long Cu₂O nanowires arrays for high-efficient water splitting applications with a convenient approach

Abstract

Abstract Nanowire (NW) structures is an alternative candidate for constructing the next generation photoelectrochemical water splitting system, due to the outstanding optical and electrical properties. NW photoelectrodes comparing to traditional semiconductor photoelectrodes shows the comparatively shorter transfer distance of photo-induced carriers and the increase amount of the surface reaction sites, which is beneficial for lowering the recombination probability of charge carriers and improving their photoelectrochemical (PEC) performances. Here, we demonstrate for the first time that super-long Cu 2 O NWs, more than 4.5 μ m, with highly efficient water splitting performance, were synthesized using a cost-effective anodic alumina oxide (AAO) template method. In comparison with the photocathode with planar Cu 2 O films, the photocathode with Cu 2 O NWs demonstrates a significant enhancement in photocurrent, from –1.00 to –2.75 mA/cm 2 at –0.8 V versus Ag/AgCl. After optimization of the photoelectrochemical electrode through depositing Pt NPs with atomic layer deposition (ALD) technology on the Cu 2 O NWs, the plateau of photocurrent has been enlarged to –7 mA/cm 2 with the external quantum yield up to 34% at 410 nm. This study suggests that the photoelectrode based on Cu 2 O NWs is a hopeful system for establishing high-efficiency water splitting system under visible light.