Four-dimensional joint visualization of electrode degradation and liquid water distribution inside operating polymer electrolyte fuel cells

Abstract

Understanding of degradation mechanisms present in polymer electrolyte fuel cells (PEFCs) is important to continue the integration of this clean energy technology into everyday life. Further comprehension of the interaction between various components during fuel cell operation is also critical in this context. In this work, a four-dimensional operando X-ray computed tomography method is developed for combined visualization of all PEFC components as well as transient water distribution residing in the cell, which results as a by-product of the electrochemical reaction. Time resolved, identical-location visualization through degradation stages is uniquely enabled by the non-invasive and non-destructive qualities of this method. By applying an accelerated stress test that targets cathode catalyst layer (CCL) corrosion, novel observations resulting from morphological changes of the CCL such as reduction in the water volume in the adjacent gas diffusion layer, CCL crack formation and propagation, membrane swelling, as well as quantification of local carbon loss is achieved. Additionally, insight into features that contribute to reduced fuel cell performance is enabled by the use of this specialized imaging technique, such as increased membrane undulation causing delamination and separation of the CCL from the microporous layer, which greatly affects liquid water pathways and overall device performance.