Promoter Effects of Functional Groups of Hydroxide-Conductive Membranes on Advanced CO₂ Electroreduction to Formate

Abstract

The electrochemical reduction of CO₂ at ambient conditions provides a latent solution of turning waste greenhouse gases into commodity chemicals or fuels; however, a satisfactory ion-conducting membrane for maximizing the performance of a CO₂ electrolyzer has not been developed. Here, we report the synthesis of a sequence of hydroxide-conductive polymer membranes, which are based on polymer composites of poly(vinyl alcohol)/Guar hydroxypropyltrimonium chloride, for use in CO₂ electrolysis. The effect of different membrane functional groups, including thiophene, hydroxybenzyl, and dimethyloctanal, on the efficiency and selectivity of CO₂ electroreduction to formate is thoroughly evaluated. The membrane incorporating thiophene groups exhibits the highest Faradaic efficiency of 71.5% at an applied potential of -1.64 V versus saturated calomel electrode (SCE) for formate. In comparison, membranes containing hydroxybenzyl and dimethyloctanal groups produced lower efficiencies of 67.6 and 68.6%, respectively, whereas the commercial Nafion 212 membrane was only 57.6% efficient. The improved efficiency and selectivity of membranes containing thiophene groups are attributed to a significantly increased hydroxide conductivity (0.105 S cm^-1), excellent physicochemical properties, and the simultaneous attenuation of formate product crossover.