Effect of Aging Time and Thickness on Low‐Temperature Degradation of Dental Zirconia

Yongxiang Zhuang, Ziyuan Zhu, Ting Jiao, Jian Sun

Journal of Prosthodontics · 2018 · 29 citations · 31 references

Open access

Abstract

A thinner Y-TZP specimen was likely to present surface defects and microcracks after aging. In addition, the flexural strengths decreased with a decrease in the thickness, a notable fact for further studies.

References

31

A Critical Evaluation of Indentation Techniques for Measuring Fracture Toughness: I, Direct Crack Measurements

G. R. Anstis, P. Chantikul, Brian R. Lawn et al. · Journal of the American Ceramic Society · 1981 · 5.4K citations

Engineering, Mechanical Engineering, Hardness +20

Phase relationships in the zirconia-yttria system

H. G. Scott · Journal of Materials Science · 1975 · 1.3K citations

Phase Transitions, Engineering, Physics +4

What future for zirconia as a biomaterial?

Jérôme Chevalier · Biomaterials · 2005 · 1.2K citations

Bionics, Engineering, Biomedical Engineering +3

Five-year clinical results of zirconia frameworks for posterior fixed partial dentures.

Irena Sailer, Aurel Fehér, Frank Filser et al. · PubMed · 2007 · 802 citations

Low-Temperature Degradation of Zirconia and Implications for Biomedical Implants

Jérôme Chevalier, Laurent Grémillard, Sylvain Deville · Annual Review of Materials Research · 2007 · 708 citations

Materials Science, Low-temperature Degradation, Zirconia Ceramics +11