Direct observation of high spin polarization in Co2FeAl thin films

Abstract

Abstract We have studied the Co 2 FeAl thin films with different thicknesses epitaxially grown on GaAs (001) by molecular beam epitaxy. The magnetic properties and spin polarization of the films were investigated by in-situ magneto-optic Kerr effect (MOKE) measurement and spin-resolved angle-resolved photoemission spectroscopy (spin-ARPES) at 300 K, respectively. High spin polarization of 58% (±7%) was observed for the film with thickness of 21 unit cells (uc), for the first time. However, when the thickness decreases to 2.5 uc, the spin polarization falls to 29% (±2%) only. This change is also accompanied by a magnetic transition at 4 uc characterized by the MOKE intensity. Above it, the film’s magnetization reaches the bulk value of 1000 emu/cm 3 . Our findings set a lower limit on the thickness of Co 2 FeAl films, which possesses both high spin polarization and large magnetization.