Tailoring the structural, morphological, optical and dielectric properties of lead iodide through Nd3+ doping

Abstract

Abstract Hexagonal single crystal nanosheets of Nd 3+ doped PbI 2 were effortlessly synthesized via microwave-assisted technique under a power of 700 W and in a duration of 15 minutes with a homogeneous morphology. X-ray diffraction, energy dispersive X-ray spectroscope, scanning electron microscope, FT-Raman, UV-Visible, photoluminescence and dielectric measurement were employed to study the product. High purity, single phase and presence of Nd 3+ doping was confirmed. SEM study confirm the formation of nanorods and single crystal nanosheets of very few nanometers in size. Robust vibrational analysis has been carried out and the observed bands are assigned to the vibration modes of E 2 1 , A 1 1 , A 1 2 , 2E 2 1 and 2E 1 1 , respectively. These bands are red-shifted when compare to the corresponding bulk values which indicate relaxed nanostructure formation and occurrence of confinement effect. The thickness of the synthesized single crystal nanosheets are found to be in the range of ~20 to 30 nm. The energy band gap was calculated and found to be 3.35, 3.34, 3.42 and 3.39 eV for pure, 1, 3 and 5% Nd 3+ doped lead iodide, respectively. The clear blue luminescence has been observed at 440 nm and 466 nm when excited at 250 nm and 280 nm respectively. Dielectric and ac electrical conductivity was also measured and discussed.