Workability enhancement of geopolymer concrete through the use of retarder

Abstract

Geopolymer concrete is a type of concrete manufactured without the addition of cement. In geopolymer concrete, along with an activator, cement as the concrete binder can be replaced by the fly ash. This will reduce global demand on cement, and therefore will reduce CO2 emission due to cement production. Thus, geopolymer concrete is commonly known as an eco-friendly concrete. Geopolymer concrete also offers a solution concerning with the utilization of the fly ash waste. However, despite of its environmental advantages, geopolymer concrete has a drawback, namelygeopolymer concrete set quickly, thus reducing its workability. This research aimed to increase the workability of geopolymer concrete by using retarder admixture (Plastocrete RT6 Plus). Retarder used varies within 0.2%, 0.4% and 0.6% of fly ash mass. As a control, geopolymer concrete without retarder (0%) were also made. Activator used in this research was Na2SiO3 mixed with NaOH 10 M solution, with ratio of 1:5. The results showed an optimum composition of geopolymer concrete with 0.6% retarder, where initial setting time occured after 6.75 hours, and the final setting time reached after 9.5 hours. Moreover, the slump of the geopolymer concrete was 8.8 cm, and the slump flow was 24 cm. The compressive strength of the geopolymer concrete at 28 days was 47.21 MPa. The experiment showed that the more retarder added, the setting time of the geopolymer concrete will be increased, thus increasing its workability.