Self-Plasticization of PVC via click reaction of a monooctyl phthalate derivative

Abstract

Abstract Modified PVC (M-PVC) material with suppressed migration and low glass transition temperature was prepared via click reaction of a monooctyl phthalate derivative. Chemical structure and composition of M-PVC were characterized by FT-IR, 1H NMR and element analysis. Thermal stability, glass transition temperature and migration stability of M-PVC were studied with TGA, DSC and migration tests, respectively. The study showed that M-PVC exhibited poor thermal stability, and low glass transition temperature of 66.0°C. No migration was found in distilled water, 10% (v/v) ethanol, 30% (w/v)acetic acid and petroleum ether. The PVC material is expected to preparing PVC products in the areas with high migration resistance requirement.