Preparation and characterization of layer‐by‐layer self‐assembly membrane based on sulfonated polyetheretherketone and polyurethane for high‐temperature proton exchange membrane

Abstract

ABSTRACT A concept of preparing high‐temperature proton exchange membranes with layer‐by‐layer (LBL) self‐assembly technique was proposed and the sulfonated polyetheretherketone (SPEEK) and polyurethane (PU) with 200 LBL deposition cycles denoting (SPEEK/PU) 200 membrane was prepared in this research. Owing to the strong electrostatic interaction between  group in SPEEK and CN + group in PU, (SPEEK/PU) 200 membrane with LBL self‐assembly structure showed a favorable structural stability. The phosphoric acid (PA)‐doped (SPEEK/PU) 200 membrane showed a higher proton conductivity relative to PA doped SPEEK/PU membrane by solution casting method (SPEEK/PU) 200 /40%PA membrane possessed a proton conductivity value of 2.90 × 10 −2 S/cm at 150 °C under anhydrous conditions. The LBL self‐assembly structure provided a possibility to reduce the negative effect from polymer skeleton blocking charge carrier species even immobilizing protons. Moreover, the (SPEEK/PU) 200 membrane presented the particularly noteworthy mechanical property even with PA doping. The tensile stress values at break were 72.8 and 24.1 MPa, respectively, for (SPEEK/PU) 200 and (SPEEK/PU) 200 /40%PA membrane at room temperature, which were obviously higher than the reported values of 15.9 and 2.81 MPa for SPEEK/PU and SPEEK/PU/60%PA membrane. © 2017 Wiley Periodicals, Inc. J. Polym. Sci., Part A: Polym. Chem. 2017 , 55 , 3446–3454