Preparation of Poly(vinylidene fluoride) Lithium‐Ion Battery Separators and Their Compatibilization with Ionic Liquid – A Green Solvent Approach

Abstract

Abstract Battery separator membranes for lithium‐ion batteries have been developed based on poly(vinylidene fluoride), PVDF, and using the “green solvent” ‐ N,N’‐dimethylpropyleneurea (DMPU). This separator presents a porous microstructure with a degree of porosity of 20 % and pore size below 1 μm, showing excellent mechanical properties. Further, its ionic conductivity, tortuosity and MacMullin number values are 0.1 mS.cm −1 , 4 and 82, respectively. This PVDF separator membrane was evaluated in Li/C–LiFePO 4 half‐cells with electrolyte solution showing good cyclability and rate capability, with a discharge value after 50 cycles of 56 mAh.g −1 at C, corresponding to 50 % of the capacity retention. Its electrochemical performance soaked in ionic liquid presents a discharge capacity of 45 mAh.g −1 at C/5‐rate and capacity retention of 60%, respectively. Thus, this separator is an appropriate candidate for environmentally friendlier and safer lithium‐ion batteries.