Gamma-radiation-induced corrosion of aluminum alloy: low dose effect

Abstract

Gamma-radiation-induced corrosion of aluminium alloy 6061 (AA6061) immersed in demineralized water was studied at radiation dose up to 206 kGy using a Co-60 gamma radiation source. The surface morphology and chemical composition of the oxide produced on the post-irradiated samples were investigated using SEM-EDS. The electrochemical corrosion potentials (Ecorr) of the post-irradiated samples were measured. The corrosion behavior of AA6061 appeared to be dose dependent under the experimental conditions. A dramatic change in surface morphology was observed in the samples exposed to gamma radiation at 206 kGy. At this radiation dose the aluminium oxide scale developed can be clearly seen. The results from electrochemical corrosion tests have shown that the corrosion potentials (Ecorr) can be undoubtedly decreased by gamma irradiation, giving corrosion rate of 7 × 10-4 mm/yr.