Real-time monitoring of the structure of ultrathin Fe3O4 films during growth on Nb-doped SrTiO3(001)

Abstract

In this work, thin magnetite films were deposited on SrTiO3 via reactive molecular beam epitaxy at different substrate temperatures. The growth process was monitored in-situ during deposition by means of x-ray diffraction. While the magnetite film grown at 400 °C shows a fully relaxed vertical lattice constant already in the early growth stages, the film deposited at 270 °C exhibits a strong vertical compressive strain and relaxes towards the bulk value with increasing film thickness. Furthermore, a lateral tensile strain was observed under these growth conditions although the inverse behavior is expected due to the lattice mismatch of −7.5%. Additionally, the occupancy of the A and B sublattices of magnetite with tetrahedral and octahedral sites was investigated showing a lower occupancy of the A sites compared to an ideal inverse spinel structure. The occupation of A sites decreases for a higher growth temperature. Thus, we assume a relocation of the iron ions from tetrahedral sites to octahedral vacancies forming a deficient rock salt lattice.