Highly Efficient Catalytic Hydrogen Evolution from Ammonia Borane Using the Synergistic Effect of Crystallinity and Size of Noble-Metal-Free Nanoparticles Supported by Porous Metal–Organic Frameworks

Abstract

A series of nonprecious metal nanoparticles (NPs) supported by metal-organic framework MIL-101 were synthesized using four methods and their catalytic performance on hydrogen evolution from ammonia borane (NH₃BH₃) was studied. The results showed that the crystalline Co NPs with size of 4.5-8.5 and 14.5-24.5 nm had low activities featuring the total turnover frequency (TOF) values of 9.9 and 4.5 mol_H2 mol_cat^-1 min^-1, respectively. In contrast, the amorphous Co NPs with size of 1.6-2.6 and 13.5-24.5 nm exhibited high activities featuring the total TOF values of 51.4 and 22.3 mol_H2 mol_cat^-1 min^-1, respectively. The remarkably different activities could be ascribed to the different crystallinity and size of Co NPs in the catalysts. Moreover, the ultrasound-assisted in situ method was also successfully applied to bimetallic systems, and MIL-101-supported amorphous CuCo, FeCo and NiCo NPs had the catalytic activities with total TOF values of 51.7, 50.8, and 44.3 mol_H2 mol_cat^-1 min^-1, respectively, which were the highest in the values of the reported non-noble metal Co-based catalysts. The present approach, namely, using the synergistic effect of crystallinity and size of metal NPs, may offer a new prospect for high-performance and low-cost nanocatalysts.