High‐Operating‐Temperature Direct Ink Writing of Mesoscale Eutectic Architectures

Abstract

High-operating-temperature direct ink writing (HOT-DIW) of mesoscale architectures that are composed of eutectic silver chloride–potassium chloride. The molten ink undergoes directional solidification upon printing on a cold substrate. The lamellar spacing of the printed features can be varied between approximately 100 nm and 2 µm, enabling the manipulation of light in the visible and infrared range. As a service to our authors and readers, this journal provides supporting information supplied by the authors. Such materials are peer reviewed and may be re-organized for online delivery, but are not copy-edited or typeset. Technical support issues arising from supporting information (other than missing files) should be addressed to the authors. Please note: The publisher is not responsible for the content or functionality of any supporting information supplied by the authors. Any queries (other than missing content) should be directed to the corresponding author for the article.