Efficient Decarbonylation of Furfural to Furan Catalyzed by Zirconia‐Supported Palladium Clusters with Low Atomicity

Abstract

Abstract Decarbonylation of furfural to furan was efficiently catalyzed by ZrO 2 ‐supported Pd clusters in the liquid phase under a N 2 atmosphere without additives. Although Pd/C and Pd/Al 2 O 3 have frequently been used for decarbonylation, Pd/ZrO 2 exhibited superior catalytic performance compared with these conventional catalysts. Transmission electron microscopy and X‐ray absorption fine structure measurements revealed that the size of the Pd particles decreased with an increase in the specific surface area of ZrO 2 . ZrO 2 with a high surface area immobilized Pd as clusters consisting of several (three to five) Pd atoms, whereas Pd aggregated to form nanoparticles on other supports such as carbon and Al 2 O 3 despite their high surface areas. The catalytic activity of Pd/ZrO 2 was enhanced with a decrease in particle size, and the smallest Pd/ZrO 2 was the most active catalyst for decarbonylation. When CeO 2 was used as the support, a decrease in Pd particle size with an increase in surface area was also observed. Single Pd atoms were deposited on CeO 2 with a high surface area, with a strong interaction through the formation of a Pd−O−Ce bond, which led to a lower catalytic activity than that of Pd/ZrO 2 . This result suggests that zero‐valent small Pd clusters consisting of more than one Pd atom are the active species for the decarbonylation reaction. Recycling tests proved that Pd/ZrO 2 maintained its catalytic activity until its sixth use.