Thin films of PZT-based ternary perovskite compounds for MEMS

Abstract

Stress free heteroepitaxial thin films of PZT-based ternary perovskite, xPb(Mn,Nb)O <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">3</sub> -(1-x)PZT, were fabricated by magnetron sputtering on (001)MgO substrates and evaluated their crystal structure, ferroelectric and piezoelectric properties. The heteroepitaxial thin films showed single c-domain /single crystal structure and exhibit hard ferroelectric behavior with large Pr, Pr=60muC/cm <sup xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</sup> , and high E <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">c</sub> , 2E <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">c</sub> =230kV/cm, at x=0.06. The PZT-based thin films exhibited high piezoelectric coupling factors k <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">t</sub> , k <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">t</sub> =70%, measured at GHz range FBAR structure. High values of mechanical quality factor Q <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">m</sub> , Q <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">m</sub> =185, were observed at 4Ghz range. The observed k <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">t</sub> and Q <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">m</sub> are, to our knowledge, the highest in the reported values. The figure of merit k <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">t</sub> <sup xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</sup> Q <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">m</sub> is almost the same to piezoelectric AlN thin films. It is confirmed the PZT-based ternary perovskite thin films have a potential for a fabrication of FBAR and/or wide band filters at GHz range.