Fabrication of 3D trench PZT capacitors for 256Mbit FRAM device application

Abstract

We fabricated trench PbZr <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">x</sub> Ti <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">1-x</sub> O <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">3</sub> (PZT) capacitors that can be used in 256Mbit 1T-1C FRAM devices. The capacitor has 0.25mum diameter and 0.4mum depth. Three layers, Ir(20nm)/PZT(60nm)/Ir(20nm), were deposited in SiO <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</sub> trench holes by ALD and MOCVD. Both columnar and granular grains were formed on the sidewalls of the trench capacitors, and their relative portion had strong size dependence. The trench capacitors with more columnar PZT grains showed good switching behavior under 2.1V external bias and 19 to 24 muC/cm <sup xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</sup> remnant polarization