Morphology and phase transformation from NaCaSiO<sub>3</sub>OH to Na<sub>2</sub>Ca<sub>2</sub>Si<sub>2</sub>O<sub>7</sub> and photoluminescence evolution via Eu<sup>3+</sup>/Tb<sup>3+</sup> doping
19
Citations
22
References
2016
Year
Crystal StructureOptical MaterialsPhotoluminescence EvolutionEngineeringSolid-state ChemistryChemistryLuminescence PropertyInorganic MaterialOptical PropertiesMaterials ScienceInorganic ChemistryPhotoluminescencePhotochemistryCrystalline DefectsCrystallographyCrystal Structure DesignApplied PhysicsCrystalsOptoelectronics
The morphologies were <italic>in situ</italic> constructed from NaCaSiO<sub>3</sub>OH to Na<sub>2</sub>Ca<sub>2</sub>Si<sub>2</sub>O<sub>7</sub>, and the dependence of their photoluminescence tuning on the Tb<sup>3+</sup>/Eu<sup>3+</sup> ratio has been discussed.