Precise Sulfite Functionalization of Polyolefins via ADMET Polymerization

Abstract

Copolymers containing sulfite functionalities precisely placed between run lengths of 8, 14, and 20 methylene units were synthesized via ADMET with weight-average molecular weights up to 40 500 g/mol (PDI = 1.89). No such polymer structures have been observed previously. The primary polymer structures and precise nature were characterized by ¹H NMR, ¹³C NMR, and IR spectroscopy. Thermal degradation temperatures up to 310 °C were observed through TGA, and melting points typical of similar unsaturated ADMET polymers were determined by DSC. X-ray scattering was used to compare the polymers to ADMET polyethylene (PE), and when the polymers have 20 carbons between sulfites, the functional groups self-assemble into layers. Higher carbon content incorporation leads to an increase in crystallinity and thermal stability for these polysulfites.