Thermochemical Formation of Polybrominated Dibenzo-<i>p</i>-Dioxins and Dibenzofurans Mediated by Secondary Copper Smelter Fly Ash, and Implications for Emission Reduction

Abstract

Heterogeneous reactions mediated by fly ash are important to polychlorinated dibenzo-p-dioxin and dibenzofuran (PCDD/Fs) formation. However, the formation of polybrominated dibenzo-p-dioxins and dibenzofurans (PBDD/Fs) through heterogeneous reactions is not yet well understood. Experiments were performed to investigate the thermochemical formation of PBDD/Fs at 150-450 °C through heterogeneous reactions on fly ash from a secondary copper smelter. The maximum PBDD/F concentration was 325 times higher than the initial PBDD/F concentration in the fly ash. The PBDD/F concentration after the experiment at 150 °C was five times higher than the initial concentration. PBDD/Fs have not previously been found to form at such a low temperature. Secondary-copper-smelter fly ash clearly promoted PBDD/F formation, and this conclusion was supported by the low activation energies that were found in Arrhenius's law calculations. Thermochemical formation of PBDD/Fs mediated by fly ash deposited in industrial facilities could explain "memory effects" that have been found for PCDD/Fs and similar compounds released from industrial facilities. Abundant polybrominated diphenyl ethers (PBDEs) that were formed through fly ash-mediated reactions could be important precursors for PBDD/Fs also formed through fly ash-mediated reactions. The amounts of PBDEs that formed through fly ash-mediated reactions suggested that secondary copper smelters could be important sources of reformed PBDEs.