International Journal of Electrochemical Science · 2016 · 11 citations · 45 references
Natural SciencesMaterials EngineeringMaterials ScienceCorrosion ScienceGreen ChemistryMetallurgyCorrosion ControlCorrosion EngineeringCorrosion InhibitorsCorrosion MechanismsCorrosion Of SteelsCorrosion-resistant MaterialsCorrosion In Acidic MediaCorrosion Inhibitor EffectsCorrosion Inhibitors For Aluminum AlloysExtractGreen Corrosion InhibitorsLow Alloy SteelsLow-alloy SteelLow-alloy Steel Corrosion
The corrosion inhibition characteristics of aqueous extract of Salvadora Persica (AESP) on low chromium-molybdenum steel (ASTM A213) grade T2 (0.5Cr- 0.5Mo) in 1M hydrochloric acid solutions has been studied chemically and electrochemically at different temperatures. The protection efficiency in absence and presence of AESP was investigated by using mass loss method, Inductively Coupled Plasma Optical Emission Spectrophotometer (ICP-OES), as will as potentiodynamic polarization, electrochemical impedance spectroscopy (EIS), and electrochemical frequency modulation (EFM) techniques. The protection efficiency was found to increase with a corresponding increase in the AESP concentration and decrease with temperature. Amongst the different adsorption isotherms, the studied compound more closely followed the Temkin isotherm. The values of standard free energy of adsorption ( ΔG o ads ) revealed that AESP is adsorbed on the low-alloy steel surface via physisorption mechanism.
45
M. Lebrini, M. Lagrenée, Hervé Vezin et al. · Corrosion Science · 2007 · 481 citations
Natural Sciences, Materials Engineering, Materials Science +17
Ramazan Solmaz, Gülfeza Kardaş, Birgül Yazıcı et al. · Colloids and Surfaces A Physicochemical and Engineering Aspects · 2007 · 388 citations
Natural Sciences, Materials Engineering, Materials Science +16