A novel low-temperature solid-state route for nanostructured cubic garnet Li<sub>7</sub>La<sub>3</sub>Zr<sub>2</sub>O<sub>12</sub> and its application to Li-ion battery
83
Citations
43
References
2016
Year
Materials ScienceMaterials EngineeringSolid-state IonicEngineeringBattery Electrode MaterialsLi-ion Battery MaterialsNanomaterialsInitial Discharge CapacityLithium-ion BatteryApplied PhysicsLi-ion BatteryEnergy StorageSolid-state RouteBatteriesChemistrySolid-state BatteryEnergy MaterialFunctional Materials
Garnet Li<sub>7</sub>La<sub>3</sub>Zr<sub>2</sub>O<sub>12</sub> nanoparticles with 1 mass% Al were prepared <italic>via</italic> a solid-state route at 750 °C within 3 h. A model cell sandwiched by Li and LiCoO<sub>2</sub> exhibited initial discharge capacity of 64 μA h cm<sup>−2</sup> μm<sup>−1</sup>, being 93% of LiCoO<sub>2</sub> theoretical value.